A tensile test uses a test specimen that has a gage length of 50 mm and an area = 200 mm2. During the test the specimen yields under a load of 98,000 N. The corresponding gage length = 50.23 mm. This is the 0.2 percent yield point. The maximum load = 168,000 N is reached at a gage length = 64.2 mm.
(a) Determine yield strength Y,
a.450 MPA
b.468 MPa
c.490 MPa
d.520 MPa
(b) Determine modulus of elasticity E
a.188.5 x 103 MPa
b.124.8 x 102 MPa
c.1885.0 x 103 MPa
d.1248.0 x 102 MPa
(c) Determine tensile strength TS.
a.740 MPa.
b.760 MPa.
c.840 MPa.
d.860 MPa
好像第一问还有点问题，0.2 percent yield point这个条件没用吗
(a) Determine yield strength Y,
a.450 MPA
b.468 MPa
c.490 MPa
d.520 MPa
(b) Determine modulus of elasticity E
a.188.5 x 103 MPa
b.124.8 x 102 MPa
c.1885.0 x 103 MPa
d.1248.0 x 102 MPa
(c) Determine tensile strength TS.
a.740 MPa.
b.760 MPa.
c.840 MPa.
d.860 MPa
好像第一问还有点问题，0.2 percent yield point这个条件没用吗
在一个拉伸试验中，样品的长度为50mm，面积是200mm2。对其施加98,000N的载荷之后，样品伸长为50.23mm。这就是0.2％的屈服点。当样品长度为64.2 mm时，外加载荷达到最大，为168,000N。
开始我还真的忘记应该怎样计算了，呵呵，所以找些资料作为参考：
弹性模量是描述固体材料抵抗形变能力的物理量。一条长度为L、截面积为S的金属丝在力F作用下伸长ΔL。F/S叫胁强，其物理意义是金属数单位截面积所受到的力；ΔL/L叫胁变其物理意义是金属丝单位长度所对应的伸长量。胁强与胁变的比叫弹性模量。http://zhidao.baidu.com/question/796140.html
（a）计算屈服强度：当然就是F/S啦，C正确
（b）计算弹性模量。我刚才发现每个结果都不对，因此我反过来将每个答案进行验证，发现50.23 mm有误，应该是50.13mm，这样选项A正确，188.5 x 103 MPa应该理解为188.5×10^3 MPa。计算方法实际上上面我引用的文字已经涉及到了，故不再重复。
（c）计算抗拉强度，计算方法和第一题相类似，C正确。
通过这道题目，偶又把大学学过的知识小小复习了一下，^_^
至于你提到的0.2 percent yield point，我认为这里是指长度大约身长了0.2％。在这个范围内材料有发生永久变形，应该属于弹性变形的范畴，因此可以利用前面的数据来计算屈服强度。超出这个范围之后，材料产生永久性变形，直至破坏，这时计算的就不是屈服强度，而是抗拉强度了。